前言：S2010,PSU,PES,PPSU,巴斯夫
物理性能额定值 (公制)额定值 (英制)测试方法密度1.24 g/cc0.0448 lb/in?ISO 1183吸水率0.80 %0.80 %ISO 62平衡吸湿0.30 %0.30 %23°C/50% R.H.; ISO 62粘度测试63 cm?/g63 cm?/gViscosity number线性成型收缩率,Flow0.0068 cm/cm0.0068 in/inISO 294线性成型收缩率，横向0.0072 cm/cm0.0072 in/inISO 294熔体流动速率90 g/10 min@Load 10.0 kg, Temperature 360 °C90 g/10 min@Load 22.0 lb, Temperature 680 °FISO 1133机械性能额定值 (公制)额定值 (英制)测试方法球压硬度135 MPa19600 psiISO 11359-1/-2抗张强度(断裂)75.0 MPa10900 psi5mm/min; ISO 527-2抗张强度(屈服)75.0 MPa10900 psi50mm/min; ISO 527-2伸长率 (断裂)5.7 %5.7 %5mm/min; ISO 527-2屈服伸长率5.7 %5.7 %50mm/min; ISO 527-2拉伸模量2.60 GPa377 ksiISO 527-2剪切模量0.0250 GPa@Temperature 200 °C3.63 ksi@Temperature 392 °FISO 67210.800 GPa@Temperature 175 °C116 ksi@Temperature 347 °FISO 67210.900 GPa@Temperature 100 °C131 ksi@Temperature 212 °FISO 67210.950 GPa@Temperature 50.0 °C138 ksi@Temperature 122 °FISO 6721悬壁梁缺口冲击强度5.00 kJ/m?2.38 ft-lb/in?ISO 180/A6.00 kJ/m?@Temperature -30.0 °C2.86 ft-lb/in?@Temperature -22.0 °FISO 180/A简支梁无缺口冲击强度NBNBISO 179/1eUNB@Temperature -30.0 °CNB@Temperature -22.0 °FISO 179/1eU简支梁缺口冲击强度0.550 J/cm?2.62 ft-lb/in?ISO 179/1eA0.0600 J/cm?@Temperature -30.0 °C0.286 ft-lb/in?@Temperature -22.0 °FISO 179/1eA拉伸蠕变模量(1000 hr)2500 MPa363000 psielongation<0.5%, 23°C; ISO 899电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率>= 1.00e+13 ohm-cm>= 1.00e+13 ohm-cmIEC 60093表面电阻>= 1.00e+14 ohm>= 1.00e+14 ohmIEC 60093介电常数3.1@Frequency 100 Hz3.1@Frequency 100 HzIEC 602503.1@Frequency 1.00e+6 Hz3.1@Frequency 1.00e+6 HzIEC 60250介电强度40.0 kV/mm1020 kV/inIEC 60243-1 3耗散因数0.00080@Frequency 100 Hz0.00080@Frequency 100 HzIEC 602500.0064@Frequency 1.00e+6 Hz0.0064@Frequency 1.00e+6 HzIEC 60250相比耐漏电起痕指数(CTI)125 V125 VTest Liquid A & B; IEC 60112热性能额定值 (公制)额定值 (英制)测试方法线性热膨胀系数53.0 ?m/m-°C@Temperature 26.0 °C29.4 ?in/in-°F@Temperature 78.8 °FDIN 5375260.0 ?m/m-°C@Temperature 125 °C33.3 ?in/in-°F@Temperature 257 °FDIN 5375265.0 ?m/m-°C@Temperature 175 °C36.1 ?in/in-°F@Temperature 347 °FDIN 53752线形热膨胀系数 - 流动53.0 ?m/m-°C@Temperature 23.0 - 80.0 °C29.4 ?in/in-°F@Temperature 73.4 - 176 °FISO 11359-1/-260.0 ?m/m-°C@Temperature 140 - 180 °C33.3 ?in/in-°F@Temperature 284 - 356 °FISO 11359-1/-2高工作温度, Air180 °C356 °Fshort cycle operations载荷下热变形温度(1.8 MPa)167 °C333 °FISO 75玻璃化转变温度，Tg187 °C369 °FISO 11357-1/-3UL RTI155 °C311 °F50% decrease of tensile strength after 20000h; 746B可燃性(UL94)HB@Thickness 1.60 mmHB@Thickness 0.0630 inV-2@Thickness 3.20 mmV-2@Thickness 0.126 in光学性能额定值 (公制)额定值 (英制)测试方法折射率1.631.631.63@Wavelength 700 nm1.63@Wavelength 700 nm1.63@Wavelength 550 nm1.63@Wavelength 550 nm1.64@Wavelength 590 nm1.64@Wavelength 590 nm1.65@Wavelength 540 nm1.65@Wavelength 540 nm1.66@Wavelength 450 nm1.66@Wavelength 450 nmTransmission, Visible89 %@Thickness 2.00 mm89 %@Thickness 0.0787 inASTM D 100375 %@Wavelength 400 nm75 %@Wavelength 400 nm85 %@Wavelength 500 nm85 %@Wavelength 500 nm85 %@Wavelength 600 nm85 %@Wavelength 600 nm紫外线透过率3.0 %@Wavelength 300 nm3.0 %@Wavelength 300 nm15 %@Wavelength 200 nm15 %@Wavelength 200 nm40 %@Wavelength 350 nm40 %@Wavelength 350 nm加工性能额定值 (公制)额定值 (英制)测试方法Adapter Temperature300 °C572 °F模具温度310 °C590 °F加工（熔体）温度330 - 390 °C626 - 734 °FInjection molding模具温度120 - 160 °C248 - 320 °FInjection moldingDie Opening110 cm43.3 in